Poled composites with Nd-Mn-doped PZTfibers under bipolar electrical load

Using the sol-gel process, Nd-Mn-doped PZT fibers were produced. The PZT was doped with 2 mol% neodymium and 1.1 mol% manganese. For characterization, the fibers were embedded in a polymer. The resulting 1-3 composites were poled with constant electric field. Strain and polarization were measured by applying a bipolar sinusoidal voltage of high amplitude. Instead of the expected shifted butterflyshaped strain hysteresis, an asymmetric strain-field relation was observed. It is characterized by a rather linear region in direction of the poling field and an inflated region without strain switching for reversed polarity. Within the temperature range from room temperature to 80°C, the strain switching seems to be suppressed. Measurements of the piezoelectric coefficient at superimposed electric field prove the blocking of strain switching. Cyclation experiments with sesquipolar load show a pronounced linearity of the strain loops that declines after more than 2 × 10
₄
cycles.