Nitrogen-Doped ZnO Film Fabricated Via Rapid Low-Temperature Atomic Layer Deposition for High-Performance ZnON Transistors

High-performance nitrogen-doped ZnO (ZnON)-based thin-film transistors (TFTs) were fabricated by atomic layer deposition (ALD) with a rapid purging time of only 5 s at a temperature as low as 150 °C. It is the first time to report ALD ZnON TFT using NH
₃
as N source. It is found that ZnON TFT with a N: Zn atomic ratio of 1:19 (ZnON 1:19) exhibited excellent properties, such as lower subthreshold swing of 0.47 V/decade and smaller ΔV
_th
of 0.71 V under the temperature stress from 25 to 105 °C. The I
_ON
and I
_OFF
decreased as N-doping concentration increased, and ZnON 1:19 TFT presented a high I
_ON
/I
_OFF
ratio of 1.75 × 10
⁷
. The density of state was calculated by temperature stress. Combining with the X-ray photoelectron spectroscopy analysis, we built a model to explain the reaction mechanism that the moderate amount of N doping could significantly suppress the creation of oxygen defects.