Degradation mechanisms and lifetime assessment of Ge Vertical PIN photodetectors

Dark current degradation mechanisms in Ge VPIN photodetectors were studied. A methodology to estimate the failure percentages has been developed and applied. Degradation/recovery processes and E
a
-decrease of I
dark
after stress suggest increased TAT during degradation.