Flexible White Lighting Fabricated With Quantum Dots Color Conversion Layers Excited by Blue Organic Light-Emitting Diodes

In this study, HATCN is coated on flexible PET/indium tin oxide (ITO) substrate as a modified layer and a hole injection layer to improve the hole injection from ITO. Then a blue organic light emitting diode (OLED) can successfully be fabricated without a surface treatment procedure (O
₂
plasma or UV Ozone treatment). The new blue TADF series fluorescent material is employed as emitting layer with a luminescence wavelength of 456 nm. Also, it has a narrow full width at a half maximum (FWHM) of 26 nm featuring excellent color chromaticity. Quantum dot (QD) photoresist is a perfect color conversion material featuring good color adjustability, narrow emission spectrum, high luminous efficiency, and simple spin-coating processes. In this study, the photoresist mixed with green and red quantum dots is used as a color conversion layer (CCL), and a blue OLED is utilized to excite green and red CCL. To test the material of QD photoresist, it is coated on the substrate of another piece of glass first and then the blue OLED is utilized to remotely excite green and red QD CCL. The fluorescence characteristic of QD photoresist is explored to acquire a spectrum of 528 nm and 620 nm. In the device structure of a blue OLED, the electron-and hole-only current density is compared and the hole transport layer TAPC thickness is adjusted to improve the luminance and efficiency. Finally, green and red quantum dot photoresist is mixed using a proper ratio and then directly coated on the back of the PET/ITO substrate. Furthermore, the thickness of the QD photoresist is adjusted to increase the QD excited fluorescence. The blue OLED and QD CCL was integrated to generate three primary colors, i.e., blue, green, and red. Finally, a flexible white OLED lighting panel is successfully fabricated using simple processes. Moreover, it features high-spectrum stability. The CIE coordinates will not drift with bias, thus, it can resist the voltage variation.