Directly Measured Electrocaloric Effect in Relaxor Polymer Nanocomposites

Composites of electroactive polymers and ferroelectric nanoparticles are promising for energy storage and electrocaloric applications. In this paper we report on synthesis and electrocaloric properties of P(VDF-TrFE-CFE)/ BaZr0.20Ti0.80O3 nanocomposites. BaZr0.20Ti0.80O3 (BZT) nanoparticles were synthesized via the hydrothermal route. The P(VDF-TrFE-CFE)/BZT composite films with varying amount (1.25 vol.% to 5 vol.%) of the nanoparticles were prepared by the solution casting method. The nanocomposite films showed a significant increase in the dielectric permittivity with the amount of nanoparticles. An increase in the polarization as well as in hysteresis losses with the amount of nanoparticles was observed. The direct electrocaloric effect was measured using a custom built quasi-adiabatic calorimeter. The P(VDF-TrFE-CFE)/BZT nanocomposite film with 5 vol.% BZT showed an electrocaloric temperature change of ~ 1.8 K at room temperature and an electric field of 50 MV/m, which is comparable to literature values.