Gate Dielectric Breakdown in A-InGaZnO Thin Film Transistors With Cu Electrodes

In this work, the impact of positive bias stress (PBS) on an all copper(Cu)-electrode a-InGaZnO TFT is discussed. Commonly, Cu diffusion from the source/drain electrode after negative bias stress (NBS) leads to degradations in the on-state current and subthreshold swing. However, this study finds that diffusion in the gate insulator layer from the gate electrode suffers from more serious degradation. Eventually, this phenomenon causes a serious breakdown of the gate insulator such that it loses the transistor function. Results indicate that after 2000s of PBS, accumulation of Cu ions forms a filament which dominates the leakage path. During the stress duration, the gate leakage current is monitored and current fittings are adopted to confirm the phenomena. Furthermore, temperature dependencies have verified the results of hopping and Ohmic conduction at different stages of deterioration. Compared to previous literature that focus on the impacts of source/drain electrodes, this work suggests that gate engineering for thin film transistors is more urgent for high-quality display applications.