Be diffusion in InGaAs/InP heterojunction bipolar transistors

Classic signatures of Be diffusion were observed in InAlAs/InGaAs HBT's after elevated temperature bias stress, i.e., a positive shift in the Gummel plot, higher collector ideality, and higher offset voltage. An activation energy of 1.57 eV was calculated. Lifetimes of 3.3/spl times/106 h and 37000 h were extrapolated for low and high power operation, respectively. In contrast, an InP/InGaAs HBT with a C doped base showed no signatures of C diffusion. The results show that Be diffusion is manageable at lower power. They also support the idea that C is more stable than Be in this material system.