Bulk growth of low resistivity n-type 4H-SiC using co-doping

The growth of n-type 4H-SiC crystal was performed by physical vapor transport (PVT) growth method by using nitrogen and aluminum (N-Al) co-doping. Resistivity of N-Al co-doped 4H-SiC was as low as 5.8 mΩcm. The dislocation densities of N-Al co-doped substrates were evaluated by synchrotron radiation X-ray topography (SXRT). In addition, epitaxial growth was performed on the N-Al co-doped substrates by chemical vapor deposition (CVD). No double Shockley type stacking fault was observed in the epitaxial layer.