Characterization of Cub2SnSe3 thin films fabricated by coevaporation

Cu
₂
SnSe
₃
(CTSe) thin films were fabricated by coevaporation on soda-tune glass substrates at the substrate temperature of 300 °C under rations Cu/Sn supply ratios. From X-ray diffraction ( XRD) analyses, diffraction peaks of CTSe with a cubic sphalerite structure were observed in all CTSe thin films. In addition, SnSe and SnSe
₂
phases were also detected in Sn-ricb CTSe thin films. On the other bands, in Cu-rich CTSe thin films, a Cu
₂