Mössbauer Studies Magnetic Properties of BaCo2−xZnxFe16O27

The BaCo
_2-x
Zn
_x
Fe
₁₆
O
₂₇
(x = 0, 0.5, 1) samples were prepared by solid-state reaction method. The prepared samples are single-phased, and their crystal structures are determined to be hexagonal with a space group of P63/mmc from Rietveld refinement analysis. The magnetic saturation values were increasing, and the values of coercivity were decreasing with increasing Zn contents. The experimentally measured temperature dependence of magnetization curves shows magnetic transitions. We have measured Mössbauer spectroscopy at various temperatures to investigate microscopic magnetic properties. We analyze the obtained spectra with the five magnetic sites of 4f
_VI
, 6g + 4f
_VI
, 4e
_IV
+ 4f
_IV
, 12k
_VI
, and 2d
_V
. In addition, from the Mossbauer spectra, we notice the changes in the magnetic hyperfine field and electric quadrupole shift. The substituted Zn
²⁺
ions are located at tetrahedral site, and increase the M
_s
. Curie temperatures were determined from zero-field-cooled magnetizations measurement.