Temperature-dependent time-resolved photoluminescence study of monocrystalline CdTe/MgCdTe double heterostructures with low defect density

Confocal photoluminescence scans of monocrystalline CdTe/MgCdTe double heterostructures epitaxially grown on lattice-matched InSb substrates reveal very low twin defect density, below 1 × 10
⁵
cm
^-2
. Room-temperature Shockley-Read-Hall (SRH) lifetimes of these samples are determined in the range of 35 ns to 86 ns using time-resolved photoluminescence (TRPL) measurements. Temperature-dependent TRPL measurements show that the carrier lifetime reaches a peak of 910 ns at 200 K. Excitation-dependent PL measurements reveal the radiative recombination coefficient of CdTe to be 4.3 × 10
^-9
cm
³
·s
^-1
.