Wafer-Bonded p-n Heterojunction of GaAs and Chemomechanically Polished N-Polar GaN

This letter reports wafer-bonded p-n heterojunction diodes, which consist of GaAs and chemomechanically polished N-polar GaN. The measured
I
-
V
and
C
-
V
show well-behaved p-n junction characteristics. The built-in voltage extrapolated from the
C
-
V
is 0.2 V less than the theoretical, suggesting the existence of interface states. However, this offset is much less than that (1.14 V) reported of wafer-bonded GaAs/Ga-polar GaN p-n diodes. The limited maximum current suggests pinning of the Fermi level at interface traps near the conduction band accessed under forward bias. Yet, this junction shows promise as a collector junction for wafer-bonded devices to achieve higher breakdown voltages.