Magnesium Diboride Wires With Nonmagnetic Matrices—AC Loss Measurements and Numerical Calculations

In the superconducting applications, the wires are exposed to time-varying magnetic field when the current changes. This generates losses which can be minimized by reducing filament size, twisting the wire, and increasing the transverse resistivity. However, the high losses of magnesium diboride wires often arise from magnetic sheath materials, and therefore, this work presents new type of wires with nonmagnetic matrix and multi-filamentary structure. The results of AC loss measurements, in external sinusoidal magnetic field, are presented. Two
${\rm MgB}_{2}$
samples were measured both in two temperature ranges, as two different set-ups were used, one with fixed LHe bath temperature 4.2 K. Second one enabled operation temperatures from 23 K up to the critical temperature of 39 K. Amplitude of magnetic field of the former set-up was up to 0.8 T and frequency range was from 0.1 to 1.4 Hz. In the latter one, the maximum amplitude was 28 mT, and the frequencies were 72 and 144 Hz. The results evidenced that the superconducting filaments were uncoupled and the measurements agreed with theoretical models based on this assumption. In practice, the uncoupling was modeled so that the net current in each filament was set to zero.