Development of non-destructive examination techniques for CFC-metal joints in annular geometry and their application to the manufacturing of plasma-facing components

The design of plasma-facing components for ITER, as for any of the envisaged next-step machines, relies heavily on the use of brazed junctions to couple armour materials to the heat sink and cooling tubes. Moreover, the typical number of brazed components and the envisaged effects of local overheating due to failure in a single brazed junction stress the importance of having a set of NDE techniques developed that can ensure the flawless quality of the joint. The qualification and application of two NDE techniques (ultrasonic and thermographic analysis) for inspection of CFC-to-metal joints is described with particular regard to the annular geometry typical of macroblock/monoblock solutions for divertor high-heat-flux components. The results of the eddy current inspection are not reported. The development has been focused specifically on the joint between carbon-fibre composite and TZM molybdenum alloy; techniques for the production of reference defect samples have been devised and a set of reference defect samples produced. The comparative results of the NDE inspections are reported and discussed, also on the basis of the destructive examination of the samples. The nature and size of relevant and detectable defects are discussed together with hints for a possible NDE strategy for divertor high-heat-flux components.