Discontinuous resistance change and domain wall scattering in patterned NiFe wires with a nanoconstriction

A nonlinear current-voltage (I-V) characteristic was observed in patterned NiFe wires with a central "bow-tie" point contact constriction. By passing a dc current through the wire, a sharp resistance drop was obtained for current densities in the range of 1.1-1.4/spl times/10/sup 7/ A/cm/sup 2/. This is attributed to current-induced domain wall drag, resulting in displacement of a domain wall away from the constriction. A maximum current-induced resistance change of 0.079% was obtained for a 100-nm constriction, which is comparable with the magnetoresistance due to domain wall scattering in NiFe.