Ultrahigh-sensitive tin-oxide microsensors for H/sub 2/S detection

Ultrahigh-sensitivity SnO/sub 2/-CuO sensors were fabricated on Si(100) substrates for detection of low concentrations of hydrogen sulfide. The sensing material was spin coated over platinum electrodes with a thickness of 300 nm applying a sol-gel process. The SnO/sub 2/-based sensors doped with copper oxide were prepared by adding various amounts of Cu(NO/sub 3/)/sub 2/.3H/sub 2/O to a sol suspension. Conductivity measurements of the sensors annealed at different temperatures have been carried out in dry air and in the presence of 100 ppb to 10-ppm H/sub 2/S. The nanocrystalline SnO/sub 2/-CuO thin films showed excellent sensing characteristics upon exposure to low concentrations of H/sub 2/S below 1 ppm. The 5% CuO-doped sensor having an average grain size of 20 nm exhibits a high sensitivity of 2.15/spl times/10/sup 6/ (R/sub a//R/sub g/) for 10-ppm H/sub 2/S at a temperature of 85/spl deg/C. By raising the operating temperature to 170/spl deg/C, a high sensitivity of /spl sim/10/sup 5/ is measured and response and recovery times drop to less than 2 min and 15 s, respectively. Selectivity of the sensing material was studied toward various concentrations of CO, CH/sub 4/, H/sub 2/, and ethanol. SEM, XRD, and TEM analyses were used to investigate surface morphology and crystallinity of SnO/sub 2/ films.