Onset of Mechanical Degradation due to Transverse Compressive Stress in Nb3Sn Rutherford-Type Cables

In the framework of the High Field Magnets program at CERN, lower limits of degradative mechanical loads on reacted and impregnated Nb
₃
Sn Rutherford-type cables are being studied with the goal of optimizing the pre-stress applied at room temperature on the accelerator magnets. Coils are loaded during assembly, for instance when transverse load is applied by using a collaring press or the bladder and key technique. Nb
₃
Sn is susceptible to transverse compressive stress, which is the loading condition investigated for this study. The purpose of this work is to identify the maximum pressure that can be applied, at room temperature, to reacted cables without generating cracks in the Nb
₃
Sn subelements and to quantify the crack propagation with increasing pressure. Metallographic techniques are used to examine the onset and evolution of damage in the transverse planes of impregnated double-stacked Rutherford-type cable specimens with increasing stress. The damage pattern observed at subelement, strand and cable levels is described. Two reaction heat treatment cycles are analyzed.