Photothermal stability of encapsulated silicon solar cells and encapsulation materials upon accelerated exposures. II

The authors studied the electrical and optical performance stability of crystalline silicon solar cells that were encapsulated with different types of EVA (ethylene vinyl acetate) between a borosilicate glass superstrate and a glass or white TPT (Tedlar/polyester/Tedlar) substrate. Total internal light reflection from the white TPT layer enhanced the measured cell photocurrent by /spl sim/20.4% to 23.9% and the efficiency by /spl sim/17.4% to 20.8%, with a cell-to-sample area ratio of 23,3%. In comparison, the enhancements on the cell photocurrent were from /spl sim/5.0% to 7.0% when the cells were laminated between two borosilicate plates. The samples were exposed under to /spl sim/6.5 UV suns at 65/spl deg/C or heated in an oven at 105/spl deg/C and periodically characterized for electrical and optical losses. The results show that, when the samples were measured without black-masking over the non-cell areas, the cell efficiency decreased by /spl sim/0.3% to 8.9% and the fill factor changed by /spl sim/0% to 6.6% after 1133-h exposures. When the non-cell areas were masked, the measured cell efficiency losses became 4.1% to 9.0% and the fill factor losses from 0.5% to 5.2%, respectively. The electrical changes are irregular for the sample cells tested and are not proportional to the optical losses of EVA/TPT bi-layer. As an example, a cell's efficiency decreased by 8.9%, whereas is NREL-V11 EVA remained clear; and another cell lost 7.1% efficiency, whereas its slow-cure A9918 EVA browned with a 12.2% loss in integrated transmittance and an increase of 31.85 in yellowness index.