Enhanced spin-valve giant magneto-resistance in non-exchange biased sandwich films

A large giant magnetoresistance (GMR) value of 7.5% has been measured in simple NiFeCo(1)/Cu/NiFeCo(2) sandwich films grown on a 30 /spl Aring/ Cr seed layer. This spin-valve GMR effect is consistent with the differential switching of the two NiFeCo layers due to an enhanced coercivity of the NiFeCo(1) layer grown on the Cr seed layer. A change in growth texture of the NiFeCo(l) layer from fcc [111] to bcc [110] crystallographic orientation leads to an increase in magnetic anisotropy and an enhancement in coercivity. The GMR value increases to 8.7% when a thin CoFe interfacial enhancing layer is incorporated. Further enhancement in GMR values up to 14% is seen in the sandwich films by nano-oxide layer formation. The specular reflection at the oxide/magnetic layer interface further extends the mean free path of spin-polarized electrons.