Electromigration after stress-induced migration test in quarter-micron Al interconnects

A sequential test of stress-induced migration and electromigration was employed to evaluate Al interconnect reliability. We investigated electromigration after storage testing for stress-induced failure and found a deterioration in electromigration lifetime of quarter-micron Al interconnects caused by slit-like voids generated during the storage test.<>