Activation Energy of Defects in Neutron Irradiated Silicon

Annealing studies of defects introduced in Si by a fast neutron flux have been made, using planar transistor samples to follow changes in minority carrier lifetime. An activation energy of 1.2 ± 0.1 eV was obtained from measurements of annealing over the range 100°C to 156°C.