Electrospun Blends of Natural and Synthetic Polymers as Scaffolds for Tissue Engineering

Engineering functional three-dimensional (3-D) tissue constructs for the replacement and/or repair of damaged native tissues using cells and scaffolds is one of the ultimate goals of tissue engineering. In this study, non-woven fibrous scaffolds were electrospun from the synthetic biodegradable polymer poly(lactic-co-glycolic acid) (PLGA) and natural proteins, gelatin (denatured collagen) and elastin. In the absence of cross-linking agent, the average PGE fiber diameter increased from 347 ± 103 nm to 999 ± 123 nm upon wetting as measured by scanning electron microscopy. Rat bone marrow stromal cells (rBMSC) were used paradigmatically to study the 3-D cell culture properties of PGE scaffolds. Consistent with the observed properties of the individual fibers, PGE scaffolds initially swelled in aqueous culture medium, however rBMSC seeded PGE scaffolds contracted to < 50% of original size. Time course histological analysis demonstrated uniform seeding of rBMSC into PGE scaffolds and complete cell penetration into the fibrous architecture over 4 weeks of in vitro culture.