Effect of intermetallic compounds on the shear fatigue of Cu/63Sn-37Pb solder joints

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Chan, Y.C. ; City Univ. of Hong Kong, Kowloon, Hong Kong ; Tu, P.L. ; So, A.C.K. ; Lai, J.K.L.

The effect of Cu-Sn intermetallic compounds (IMC) on the fatigue failure of solder joints has been studied by means of shear cycling. The samples consist of leadless ceramic chip carriers (LCCC) soldered onto FR-4 printed circuit boards (PCB), and are prepared by conventional reflow soldering using a 63Sn-37Pb solder paste and then aged at 150°C for 1, 4, 9, 16, 25, 36, and 49 days. The specimens are subjected to low cycle fatigue shear tests controlled by the displacement. The results indicate that the fatigue lifetime of the solder joints depends on the thickness of the LMC layer between the Cu-pad and bulk solder, and the quantitative relationship between the lifetime and thickness can be described as a monotonically decreasing curve. The greatest decrease is over the thickness range up to 2.8 μm, when the IMC/bulk solder interface becomes flat, corresponding to a lifetime decrease to 62% of the as assembled value. For further increase in IMC thickness the lifetime decreases more slowly. Evidently, the effect of the Cu-Sn intermetallic compounds on the joint fatigue lifetime is not only concerned with the IMC thickness hut also the interface morphology. A thick and flat LMC layer has a deleterious effect. The results of X-ray diffraction and metallographic analysis show that cracks initiate underneath the component metallization, and propagate along the IMC/solder interface, then toward the fillet. The Cu 3Sn (ε-phase) is formed between the Cu-pad and p-phase, and grows more quickly than the η-phase during storage and long term operation or aging tests. However, the Cu3Sn makes only a small direct contribution toward fatigue failure

Published in:

Components, Packaging, and Manufacturing Technology, Part B: Advanced Packaging, IEEE Transactions on  (Volume:20 ,  Issue: 4 )

Date of Publication:

Nov 1997

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.