Stability of ITO Thin Film on Flexible Substrate Under Thermal Aging and Thermal Cycling Conditions

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

7 Author(s)
Hamasha, M.M. ; Dept. of Syst. Sci. & Ind. Eng., State Univ. of New York at Binghamton, Binghamton, NY, USA ; Dhakal, T. ; Alzoubi, K. ; Albahri, S.
more authors

Indium-tin-oxide (ITO) is a transparent conductive thin film that is widely used as a top conducive layer in photovoltaic solar cells. However, ITO is sensitive to environmental conditions and the electrical conductivity degrades as a consequence of harsh environmental conditions. Furthermore, the thermal expansion coefficient mismatch between the ITO film and the substrate creates stress/strain on the film when the package is subjected to fluctuating temperatures. This could create micro-cracks and consequently damage the film. Therefore, this study was designed to study the effect of the thermal cycling and thermal aging on the ITO thin films to simulate the effect of continuous high temperatures and fluctuating temperatures that may be applied on the thin films during the usage. In this study, two sets of experiments were conducted on a 60Ω/□square sputter-deposited ITO on 127 μm heat stabilized Poly Ethylene Terephthalate (PET) substrate. The first set of experiments contained four samples which were thermally aged at 100°C for 30 days and the other set of experiments contained another four samples which were thermally cycled for 900 cycles. The thermal profile consisted of a high temperature of 100°C, a low temperature of 0°C, dwell time of 10 minutes, and ramp rate of 10°C/min , as depicted in Fig. 1. The initial results showed that the ITO thin film is not stable in the thermal aging experiment and the electrical resistivity gradually increased for all samples until the end of the 30 days. The degradation happened during the thermal cycling as well. However, SEM images show that the morphology of the ITO surface is stable under both conditions. Energy-dispersive X-ray (EDX) spectroscopy analysis showed stability in the ITO thin film in terms of composition. XRD spectra confirmed the improved crystallinity for the thermally aged films, which corresponded to the- increased transmission in the visible region.

Published in:

Display Technology, Journal of  (Volume:8 ,  Issue: 7 )

Date of Publication:

July 2012

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.