Effects of the crystallographic orientation of Sn grain during electromigration test

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

7 Author(s)
Kiju Lee ; ISIR, Osaka Univ., Ibaraki, Japan ; Keun-Soo Kim ; Yamanaka, K. ; Tsukada, Y.
more authors

The relationship between electromigration behavior and the crystallographic orientation of Sn grains was investigated. The test vehicle was the Cu/Sn-3.0wt%Ag-0.5wt%Cu/Cu dummy flip-chip model, and the applied current density was 15 kA/cm2 at 160°C. The depletion of Cu atoms at the cathode side is a major cause of the early circuit failure. Electromigration behavior and the growth of intermetallic compounds were strongly depend on the orientation of Sn grains with respect to the electron flow. Rapid failure occurred when the c axis of Sn grains close to the parallel to the direction of the electron flow, due to the Cu depletion at the cathode side. Slight microstructural changes and improved electromigration properties were observed when the c axis of the Sn grains close to perpendicular to the direction of electron flow.

Published in:

CPMT Symposium Japan, 2010 IEEE

Date of Conference:

24-26 Aug. 2010

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.