Systematic Study on Filament Fracture Distribution in ITER {\hbox {Nb}}_{3}{\hbox {Sn}} Strands

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

5 Author(s)
Nijhuis, A. ; Fac. of Sci. & Technol., Univ. of Twente, Enschede, Netherlands ; Miyoshi, Y. ; Jewell, M.C. ; Abbas, W.
more authors

In ITER CICCs, the strands experience varying mechanical strain levels due to thermal compression and electromagnetic loading, cumulating into severe periodic bending and contact strain. Depending on the choice of the cabling pattern, the strain may exceed the irreversibility limit leading to cracks in the Nb3Sn filaments and degraded performance of the conductors. We present a systematic microscopy study of filament fracture at gradually varied axial tensile strain levels in a bronze and internal tin processed type of Nb3Sn ITER strand. The axial stress-strain relation of the wires was measured at 4.2 K, up to a different peak load for each sample, successively increasing from 0.0% to 0.7%. Longitudinal cross sections were prepared from cut sections of the specimens. The crack pattern and distribution in the isolated filaments could thus be studied as a function of applied strain, revealing different fracture mechanisms. Electrical measurements were performed with applied strain with special attention for the tensile strain range. Finally, the microscopic information was correlated back to the observed macroscopic I c degradation.