Low temperature crystallization of high permittivity Ta oxide using an Nb oxide thin film for metal/insulator/metal capacitors in dynamic random access memory applications

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

6 Author(s)
Ma, Dongjoon ; Department of Nano Science and Technology, Sejong University, 98 Gunja-Dong, Gwangjin-gu, Seoul 143-747, Korea ; Park, Sungho ; Seo, Bum-Seok ; Choi, SangJun
more authors

Your organization might have access to this article on the publisher's site. To check, click on this link:http://dx.doi.org/+10.1116/1.1829060 

(Ta1-xNbx)2O5 as the dielectric for metal/insulator/metal capacitors with Ru electrodes were investigated. Deposition was performed by ALD using tantalum ethoxide, niobium ethoxide, and ozone as source materials. The high-κ dielectric layer was synthesized from a binary layer (Ta2O5/Nb2O5) with self-diffusion of the seed layer, Nb2O5. The seed layer becomes effective at a thickness of over 60 Å. The dielectric deposited with 60 Å Nb2O5 crystallized at 575 °C, the lowest processing temperature required to achieve good step-coverage (86%) for future generation dynamic random access memory. A capacitance density of about 23.0 fF/μm2 was observed for seed layers of 20 and 35 Å. Capacitors with a Nb2O5 seed layer of 60 Å achieved a capacitance density as high as 44.2 fF/μm2. The reason for this disparity is that the thicker insulator crystallizes at a post-annealing temperature of 575 °C. The leakage current measured at 1 V was moderately low, near 1×10-7 A/cm2.

Published in:

Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures  (Volume:23 ,  Issue: 1 )

Date of Publication:

Jan 2005

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.