Chemical vapor deposition of fluoroalkylsilane monolayer films for adhesion control in microelectromechanical systems

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

The purchase and pricing options are temporarily unavailable. Please try again later.
5 Author(s)
Mayer, T.M. ; Sandia National Laboratories, Albuquerque, New Mexico 87185 ; de Boer, M.P. ; Shinn, N.D. ; Clews, P.J.
more authors

Your organization might have access to this article on the publisher's site. To check, click on this link:http://dx.doi.org/+10.1116/1.1288200 

We have developed a new process for applying a hydrophobic, low adhesion energy coating to microelectromechanical (MEMS) devices. Monolayer films are synthesized from tridecafluoro-1,1,2,2- tetrahydrooctyltrichlorosilane (FOTS) and water vapor in a low-pressure chemical vapor deposition process at room temperature. Film thickness is self-limiting by virtue of the inability of precursors to stick to the fluorocarbon surface of the film once it has formed. We have measured film densities of ∼3 molecules nm2 and film thickness of ∼1 nm. Films are hydrophobic, with a water contact angle ≫110°. We have also incorporated an in situ downstream microwave plasma cleaning process, which provides a clean, reproducible oxide surface prior to film deposition. Adhesion tests on coated and uncoated MEMS test structures demonstrate superior performance of the FOTS coatings. Cleaned, uncoated cantilever beam structures exhibit high adhesion energies in a high humidity environment. An adhesion energy of 100 mJ m-2 is observed after exposure to ≫90% relative humidity. Fluoroalkylsilane coated beams exhibit negligible adhesion at low humidity and ≤20 μJ m-2 adhesion energy at ≫90% relative humidity. No obvious film degradation was observed for films exposed to ≫90% relative humidity at room temperature for ∼24 h. © 2000 American Vacuum Society.