15% multicrystalline n-type silicon screen-printed solar cells with Al-alloy emitter

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$33 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

6 Author(s)
Frederic Dross ; IMEC vzw, Kapeldreef 75, B-3001 Leuven, Belgium ; Ronald H. Franken ; Sukhvinder Singh ; Emmanuel van Kerschaver
more authors

Long diffusion length is essential to reach high efficiencies (≫15%) on rear-junction solar cells. As a rule of thumb the minority carrier diffusion length should be at least three times as long as the wafer thickness. Thanks to the smaller capture cross-section of impurities measured in n-type material, n-type silicon can exhibit a diffusion length exceeding 600 μm even in its multi-crystalline form. High-efficiency rear-junction cells become feasible at reasonable cost with wafers as thick as 200 μm. The development of the p+ emitter on the rear is essential for this type of cell, and Al alloying is one of the techniques of choice to realize it. After optimizing the emitter, we obtained very good values for Voc (∼615 mV) and FF (≫80%). Afterwards, focus was laid on improving the short-circuit current. This was achieved by an optimization of the phosphorus-diffused front-surface field, and by thinning down the wafers. These two actions had the consequence of increasing independently of each other the Jsc by 2.3−2 for the optimization of the front-surface field, and by 3−2 when wafer thickness decreased from 300 μm to 150 μm. The characteristics obtained are observed to be extremely dependent on the wafer quality, which varies a lot along the ingot. An efficiency of 15.0% (30.7−2) was reached on rear-junction n-type 150-μm-thick 5×5-cm2 multi-crystalline Si.