Growth and properties of ruthenium based metal gates for pMOS devices

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

6 Author(s)

Thinfilms of Ru, RuG2 and SrRu03 were prepared/or application as metal gates for sub-micrometer CMOS technology. The films were grown by metal organic chemical vapour depOSition at temperatures from 300 to 500 °C Room temperature resistivity of the depositedfilms rangedfrom 20 μΩcm for Ru up to 1 mS2cm for SrRu03. Stability of the gate electrodes in forming gas (90%N2+10%H2) and nitrogen atmosphere was examined. Optimised Ru, RuO2 and SrRu0Msub>3 films were then depOSited on ALD (atomic-layer deposition) grown Hf02 dielectric films. Metal-oxide-semiconductor (MGS) structures were prepared using wet and ion beam etching 0/ upper electrodes. Work junction of the Ru-based metal gate electrodes extracted from the capacitance-voltage measurements was found to be close to 5 eV for all studied MOS structures.