A new magnetic alloy of high constant permeability

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Ying-Shan Yang ; Central Iron and Steel Institute, Beijing, China ; Wang, C. ; Chen, X. ; Wang, Z.

Several conventional alloys of constant permeability used previously were of lower values of permeability, or they would change obviously in different intensities of magnetic field and thus could not satisfy some specific requirements of electrical application. The alloys consisted of Ni 60-70 wt%, Fe 29-39wt% and Mn 0-1 wt% were investigated. The best of those alloys for certain use is 1J66 alloy in China. It is a new alloy of high constant permeability with the chemical composition as Fe 34 wt%, Ni 65 wt% and Mn 1 wt%. Its AC induction permeability \mu_{L}= 3400 G/Oe ( f=60 Hz). Within the range of Bm=20-6800 G, the stability of AC induction permeability ( f=60 Hz) \alpha _{\sim} = 4.3 %. The α is defined as \alpha = \mu\max -\mu\min/\mu\min,\alpha \max and \mu\min are the maximum and the minimum of permeability respectively in the range of given magnetic field. The temperature stability αTof μLwithin the range of temperature from -60°C to +90°C is 2.9%. The saturation magnetic induction of 1J66 alloy equals 13500 G. The remanence B_{r} < 150 G. The coercive force H_{c} = 0.05 Oe. The oxygen content of 0.015- 0.04% in the alloy is considered necessary for obtaining a good stability of permeability.