Soft magnetic properties of nanocrystalline amorphous HITPERM films and multilayers

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Huang, M.-Q. ; Dept. of Mater. Sci. & Eng., Carnegie Mellon Univ., Pittsburgh, PA, USA ; Hsu, Y.-N. ; McHenry, M.E. ; Laughlin, D.E.

Amorphous precursors to HITPERM (Fe, Co)-Zr-B-Cu (a-HITPERM) films and a-HITPERM/SiO2 multilayer films have been deposited on glass or Si substrates by a rf sputtering system with a target of composition (Fe0.7Co0.3)88Zr7B4 Cu1. It was found that the a-HITPERM single layer film with a thickness of 100 mm possessed good soft magnetic properties with a saturation magnetization of 4πMs⩾14 kG and a coercivity of Hc~0.9 Oe at room temperature. Hc increases from 0.9 Oe to 25 Oe when the him thickness increases from 100 to 150 nm. To obtain excellent soft magnetic properties at larger thicknesses, a-HITPERM/SiO2 multilayer films have been synthesized. In these, Hc drops from 25 Oe (single layer) to 0.25 Oe (multilayers) with the same total a-HITPERM thickness. The intervening SiO2 layers play an important role in reducing the coercivity. Experimental results show the optimum thickness for SiO2 was 2-4 nm. M-H loops for the multilayers films exhibit pronounced two step magnetization reversal processes for temperatures between 5 and 25 K. This behavior can be attributed to magneto-static coupling between a-HITPERM layers and sequential switching of the layers. The coupling exhibits itself in a blocked phenomenon with wide (stepped) hysteresis curves for T<25 K and smooth narrow hysteresis curves for T>25 K. The effects of magneto-static coupling on the magnetic properties of a-HITPERM/SiO2 films will be discussed

Published in:

Magnetics, IEEE Transactions on  (Volume:37 ,  Issue: 4 )

Date of Publication:

Jul 2001

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.