A 50-m long, biaxially textured NiO buffer layer for epitaxial growth of YBa2Cu3O7-δ(YBCO) film has been fabricated on a long length cube-textured Ni tape using the surface-oxidation epitaxy (SOE) technique. The thickness of NiO layer was arranged to be around 3 μm. The tape manufacturing speed was 15 m/h, The SOE-NiO layer was highly (100) oriented and the full width at half maximum from the X-ray φ-scan for NiO(111) was varied from 13 to 19 degrees in the whole length. Jc values exceeding 0.3 MA/cm2 at 77 K and self field have been obtained in short samples of YBCO films on NiO/Ni tapes, by using a thin MgO cap layer with the thickness of about 100 nm. Crystal orientation control of YBCO coated conductors by the SOE method is very effective even for the long length Ni tapes
Published in:
Applied Superconductivity, IEEE Transactions on
(Volume:11
,
Issue:
1
)
Date of Publication: Mar 2001
- Page(s):
- 3138 - 3141
- ISSN :
- 1051-8223
- INSPEC Accession Number:
- 6942937
- Digital Object Identifier :
- 10.1109/77.919728
- Product Type:
- Journals & Magazines
- Date of Current Version :
- 07 August 2002
- Issue Date :
- Mar 2001
- Sponsored by :
- The IEEE Council on Superconductivity
About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies
A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2013 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.