Cart (Loading....) | Create Account
Close category search window
 

Silicon carbide micro-reaction-sintering using micromachined silicon molds

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

5 Author(s)
Tanaka, S. ; Dept. of Mechatronics & Precision Eng., Tohoku Univ., Sendai, Japan ; Sugimoto, S. ; Li, Jing-Feng ; Watanabe, R.
more authors

This paper describes a novel process, “silicon carbide micro-reaction-sintering,” to reaction-sinter three-dimensional silicon carbide microstructures using micromachined silicon molds. This process consists of micromachining of silicon molds, filling the molds with material powders (α-silicon carbide, graphite and phenol resin), bonding of the molds with adhesive, reaction-sintering by hot isostatic pressing (HIP) and release of a reaction-sintered workpiece from the mold by wet etching. Using this process, we have successfully fabricated silicon carbide microrotors with a diameter of 5 and 10 mm for a micromachined gas turbine. The shape of the silicon molds could be well transferred to the reaction-sintered samples within 3% shrinkage of the size. We used scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis to evaluate the reaction-sintered samples. They revealed the generation of β-silicon carbide by the reaction between silicon and graphite in reaction-sintering process. They also revealed the presence of residual free silicon in the reaction-sintered samples due to low concentration of graphite in the material powders. We measured mechanical properties such as bending strength and Vickers hardness. The reaction-sintered samples had approximately 70% bending strength and 70-80% Vickers hardness compared with those of a commercially-available reaction-sintered silicon carbide

Published in:

Microelectromechanical Systems, Journal of  (Volume:10 ,  Issue: 1 )

Date of Publication:

Mar 2001

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.