On the degradation of InGaAsP/InP-based bulk lasers

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Kallstenius, Thomas ; Mater. Sci. Div., Uppsala Univ., Sweden ; Backstrom, J. ; Smith, Ulf ; Stoltz, B.

Degradation of InGaAsP-InP-based buried-heterostructure bulk (BH-bulk) lasers has been studied by means of electroluminescence (EL), photoluminescence (PL), electron-beam-induced current (EBIC) and transmission electron microscopy (TEM). Lasers with p/n as well as semi-insulating (SI) current-blocking layers were studied. The results show that moderate increases in the threshold current correlate well with formation of dark defects (DD's) (i.e., dark-line defects (DLD's) or dark-spot defects (DSD's), which cannot be distinguished in our case due to the narrowness of the laser stripe.) The DD's were found to be caused by dislocation loops. The dependence of threshold current increase on the number of DD's is explained in terms of a model which includes effects due to the DD's, as well as changes in the regions outside the DD's. The latter is found to be responsible for the major part of the threshold current increase. Values for the ratio between the carrier lifetimes inside and outside the DD's are presented, for the first time. In our lasers, strong degradation differs from moderate degradation in that DD's do not form during aging. The presence of dislocation loops only at the sidewalls of the active stripe in lasers with p/n current-blocking layers points to the sidewalls as being critical. The near absence of dislocation loops and the smaller increase in threshold current in SI lasers which have degraded strongly, compared to the strongly degrading p/n lasers, suggest that strong degradation is a synergistic combination of damage in the sidewalls and Zn indiffusion from the current-blocking layers

Published in:

Lightwave Technology, Journal of  (Volume:17 ,  Issue: 12 )

Date of Publication:

Dec 1999

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.