Processing dependence of biaxial texture in yttria-stabilized zirconia by ion-beam-assisted deposition

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

3 Author(s)
Chudzik, M.P. ; Div. of Energy Technol., Argonne Nat. Lab., IL, USA ; Lanagan, M.T. ; Kannewurf, C.R.

Biaxially textured yttria (8 mol%)-stabilized zirconia (YSZ) thin films were deposited on randomly oriented Hastelloy C and Stainless Steel 304 at room temperature as a buffer layer for subsequent deposition of oriented YBa/sub 2/Cu/sub 3/O/sub x/ films. The 0.16-1.3 /spl mu/m thick YSZ films were deposited by e-beam evaporation at rates of 1.2-3.2 /spl Aring//sec. Biaxially textured films were produced with an Ar/O/sub 2/ ion beam directed at the substrate during film growth. X-ray diffraction was used to study in-plane and out-of-plane orientation as a function of ion bombardment angle, film thickness, ion-to-atom flux ratio, and substrate material. In-plane and out-of-plane average-misorientation angles on these YSZ films that were deposited by ion-beam-assisted deposition were as low as 17 and 5.4/spl deg/, respectively, on as-received substrates.