A study on the effect of surface roughness on the strength of single lap joints

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

2 Author(s)
Gomatam, R. ; Dept. of Polymer Eng., Akron Univ., OH, USA ; Sancaktar, E.

Summary form only given. Many surface treatments to improve adhesion roughen the surface. Treatments such as abrasion and etching remove the weak boundary layer and improve wetting behavior. Liquid adhesives that are spread during application do not ensure removal of air from cavities on the surface. Adhesive penetration into substrate pores is influenced by capillary forces and retarded by viscosity. Surface roughness can affect adhesive spreading and contact angle. In order to investigate aspects of surface roughness, surface profile, resin viscosity, and surface morphology, experiments were conducted using two steels (1018 cold rolled and hot rolled weld steel). Four surface modifications were performed on these samples by grit blasting at 552 kPa and 276 kPa from a distance of 25.4 mm and chemical etching using chromic acid for 2 mins and 10 mins. Crossed patterns were also obtained by an etch technique which involved changing the metal sample dip angle into the etch solution. Two resins were used to assess viscosity effects in interaction with different surface topographies. Contact angles were measured on all surfaces using these resins. Metal specimens were bonded under pressure and oven cured at 121°C for 2 hours. To gain insight into the effect of surface topography, SEM was used to observe the modified surfaces. Average roughness was measured using a profilometer and surface profiles were obtained for all samples. The strength and displacement values were measured at crosshead speeds of 1 and 100 mm/min, to assess the interrelation between failure mechanisms and joint displacements, surface topography and resin viscosity

Published in:

Adhesive Joining and Coating Technology in Electronics Manufacturing, 1998. Proceedings of 3rd international Conference on

Date of Conference:

28-30 Sep 1998

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.