Composite and multilayered TaOx-TiOy high dielectric constant thin films

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

6 Author(s)
Nielsen, M.C. ; Center for Integrated Electron., Rensselaer Polytech. Inst., Troy, NY, USA ; Jin-Young Kim ; Rymaszewski, Eugene J. ; Lu, Toh-Ming
more authors

A novel low temperature deposition process using reactive pulsed dc magnetron sputtering has been developed to deposit thin dielectric films composed of either a composite or alternating layers of tantalum oxide and titanium oxide. Capacitors fabricated from these dielectric materials have been found to exhibit exceptional electrical properties. For the composite material, one film containing 22% TiOy had a high dielectric constant of 38, a leakage current density of 10-6 A/cm2 at 0.5 MV/cm, and a relatively high breakdown field strength of 2.3 MV/cm. By a slight modification of the deposition conditions, alternating layers of tantalum oxide and titanium oxide were deposited to form a high dielectric constant material. The electric at properties of these films were also exceptional: a dielectric constant of 44, a leakage current density of 3.4·10-8 A/cm2 at 0.5 MV/cm, and a breakdown field strength of 2.3 MV/cm. These films have potential applications in memory and advanced electronics packaging

Published in:

Components, Packaging, and Manufacturing Technology, Part B: Advanced Packaging, IEEE Transactions on  (Volume:21 ,  Issue: 3 )