High-pressure Raman scattering study of defect chalcopyrite and defect stannite ZnGa2Se4

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

11 Author(s)
Vilaplana, R. ; Centro de Tecnologías Físicas: Acústica, Materiales y Astrofísica, MALTA Consolider Team, Universitat Politècnica de València, 46022 València, Spain ; Gomis, O. ; Perez-Gonzalez, E. ; Ortiz, H.M.
more authors

Your organization might have access to this article on the publisher's site. To check, click on this link: 

High-pressure Raman scattering measurements have been carried out in ZnGa2Se4 for both tetragonal defect chalcopyrite and defect stannite structures. Experimental results have been compared with theoretical lattice dynamics ab initio calculations and confirm that both phases exhibit different Raman-active phonons with slightly different pressure dependence. A pressure-induced phase transition to a Raman-inactive phase occurs for both phases; however, the sample with defect chalcopyrite structure requires slightly higher pressures than the sample with defect stannite structure to fully transform into the Raman-inactive phase. On downstroke, the Raman-inactive phase transforms into a phase that could be attributed to a disordered zincblende structure for both original phases; however, the sample with original defect chalcopyrite structure compressed just above 20 GPa, where the transformation to the Raman-inactive phase is not completed, returns on downstroke mainly to its original structure but shows a new peak that does not correspond to the defect chalcopyrite phase. The pressure dependence of the Raman spectra with this new peak and those of the disordered zincblende phase is also reported and discussed.