The effect of varying the Cu/Au ratio on the thermal-cycle fatigue life of 95/5 PbSn bumps

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

3 Author(s)
Haji-Sheikh, M.J. ; Honeywell Micro Switch, Richardson, TX, USA ; Ulz, D. ; Campbell, M.

The MICRO SWITCH Division of Honeywell adopted the IBM C4 flip chip die attach method for its underhood automotive applications in the mid to late 1970's. There has been a gradual increase in the reliability of IC-ceramic solder joints. This experiment shows the effect of the interface metallurgy on the thermal-cycle fatigue life of C4 technology. Samples are manufactured using a standard industry technique first pioneered by IBM. Included are results from initial experimentation on post processed bump limiting metallurgy (BLM), and mechanical data on two different sizes of IC with the variation of gold thickness. Assemblies were exposed to a thermal-cycle temperature range of -40°C to 150°C. In the initial tests, half of each wafer is placed in 1/1 concentrated H2O2/Acetic to remove the PbSn bump and expose the BLM. The etched samples are SEM/EDS analyzed for interfacial constituents. A comparison of the interface morphologies and the thermal-cycle fatigue life are shown. These results show that for extended thermal-cycle life times (>1000) that the Cu thickness of 1.2 μm and an Au thickness of 0.08 μm which is reduced from the initial 0.15 μm of our standard process is optimal. This is due to the reduced Au incorporation in the copper-tin intermetallic which produces an increase in the fatigue life and strength of the joints

Published in:

Components, Packaging, and Manufacturing Technology, Part A, IEEE Transactions on  (Volume:20 ,  Issue: 4 )

Date of Publication:

Dec 1997

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.