Effect of magnetic field annealing on magnetic properties for nanocrystalline (Fe1-xCox)78.4Si9B9Nb2.6Cu1 alloys

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

The purchase and pricing options are temporarily unavailable. Please try again later.
5 Author(s)
Wen, Zhuan-ping ; School of Science, Tianjin University, Tianjin 300072, People''s Republic of China ; Wang, Zhi ; Shi, Rui-min ; Wang, Jia
more authors

Your organization might have access to this article on the publisher's site. To check, click on this link:http://dx.doi.org/+10.1063/1.4795620 

The crystalline volume fraction Vcry, saturation magnetostriction λs, effective magnetic anisotropy 〈K〉, and temperature dependence of initial permeability (μi-T curves) for magnetic and nonmagnetic annealed (Fe1-xCox)78.4Si9B9Nb2.6Cu1 (x = 0.35, 0.5, 0.65, 1) alloys were investigated. The results showed that the magnetic annealing can enhance the Vcry and significantly reduce the λs. The Co content has an obvious effect on the λs and 〈K〉, the largest 〈K〉 was observed for the x = 0.5 magnetic annealed sample, which can be explained with magnetic atoms pair ordering theory. And the best high-temperature magnetic softness was obtained for x = 0.35 magnetic annealed sample, in which the lower λs and larger Vcry were observed.