Monofilament \hbox {MgB}_{2} Wire for a Whole-Body MRI Magnet: Superconducting Joints and Test Coils

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

7 Author(s)
Jiayin Ling ; Francis Bitter Magn. Lab., Massachusetts Inst. of Technol., Cambridge, MA, USA ; Voccio, J. ; Youngjae Kim ; Seungyong Hahn
more authors

This paper presents recent results from our continued development of a 0.5 T whole-body MRI magnet at the Francis Bitter Magnet Laboratory. HyperTech Research Corp. (Columbus, OH) manufactures the MgB2 conductor for this project. During the past year, we have found that our technique, originally developed successfully to splice unreacted multifilament MgB2 wires, works much better, i.e., of higher reliability, with unreacted monofilament MgB2 wires. This has led us to wind the entire coil components in our persistent-mode MRI magnet with unreacted monofilament MgB2 wire, having a MgB2 core of 0.4 mm in diameter, an overall diameter of 0.8 mm bare, 1 mm S-glass insulated. To verify that these coils would not suffer from flux jumping, as they would if wound with monofilament NbTi wire, magnetization studies were performed on monofilament wires of MgB2 and NbTi (as a reference) at 4.2 K. For the monofilament MgB2 wire, the results were affirmative. To further ensure the absence of flux jumping that may quench these current-carrying coils, two test coils were wound with unreacted monofilament MgB2 wire. One MgB2 coil was operated in driven mode, while the other MgB2 coil, equipped with a persistent current switch and terminated with a superconducting joint, was operated in persistent mode. The operating temperature range was 4.2-15 K for these MgB2 coils. The driven mode coil was operated in self-field. The persistent mode coil achieved a persistent current of 100 A, corresponding to a self-field of ~ 1 T in the winding, for 1 hour with no measurable decay. Both test coils were operated quench free.

Published in:

Applied Superconductivity, IEEE Transactions on  (Volume:23 ,  Issue: 3 )

Date of Publication:

June 2013

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.