Optoelectronic properties in vertically aligned ZnO/Si-nanopillars

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

9 Author(s)
Hsin-Yi Lee ; Nat. Synchrotron Radiat. Res. Center, Hsinchu, Taiwan ; Yuan-Ming Chang ; Wen-Shou Tseng ; Pin-Hsu Kao
more authors

An effective method of fabricating vertically aligned silicon nanopillars (Si-NPs) was realized by using the self-assembled silver nanodots as natural metal-nanomask for subsequent etching process. Ultrathin (~9 nm) ZnO films were deposited on the Si-NPs by atomic layer deposition to enhance the field emission property. The turn-on field defined by the 10 μA/cm2 current density criterion is ~ 0.74 V/μm with an estimated β ~ 1.33×104. The low turn-on field and marked enhancement in β were attributed to the small radius of curvature, high aspect ratio, and perhaps more importantly, proper density distribution of the ZnO/Si-NPs. On the other hand, room-temperature ultraviolet (UV) luminescence was investigated for the atomic layer deposited ZnO films grown on Si nanowires fabricated by self-masking dry etching in hydrogen-containing plasma. For films deposited at 200°C, an intensive UV emission corresponding to free-exciton recombination was observed with a nearly complete suppression of the defect-associated broad visible range emission peak.