Practical FeCo Films for Perpendicular Writer Pole

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

5 Author(s)
Inturi, V. ; Seagate Technol., Bloomington, MN, USA ; Huaqing Yin ; Kief, M. ; Hadley, M.
more authors

An attempt is made in this publication to review various developments of FeCo films for recording heads in the last decade and to look at emerging developments regarding these films. A series of FeCo films from 100% Fe to 100% Co was sputter deposited, characterized, and analyzed for various magnetic properties such as magnetostriction, uniaxial anisotropy, coercivity, dispersion, and saturation magnetization. Many process parameters, with the most influencing parameter being sputter pressure, play an important role especially influencing dispersion and/or hard axis coercivity (Hch) in these materials. Out of the many developments to date the effect of seed layer(s) in reducing grain size of high moment bcc FeCo films is still intriguing and, hence, a comprehensive review and analysis of seed layer effects are included. Although film stress can play an important role in optimizing Hch, there is no clear trend seen between film stress and Hch when viewed across broad processing conditions. Higher Hk evolution with oblique deposition is an interesting phenomenon in these films. Uniaxial anisotropies of nearly 1000 Oe were found. The anisotropy evolution is explained through magnetoelastic energy and through crystal structure. Even though these films are very columnar in nature it was found that there was little to no fiber texture present in these films and there was no difference in texture between fine grained and coarse grained FeCo films.

Published in:

Magnetics, IEEE Transactions on  (Volume:48 ,  Issue: 5 )

Date of Publication:

May 2012

Need Help?


IEEE Advancing Technology for Humanity About IEEE Xplore | Contact | Help | Terms of Use | Nondiscrimination Policy | Site Map | Privacy & Opting Out of Cookies

A not-for-profit organization, IEEE is the world's largest professional association for the advancement of technology.
© Copyright 2014 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.