Nanocrystalline Soft Magnetic Fe-Si-B-P-Cu Alloys With High B of 1.8–1.9T Contributable to Energy Saving

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

1 Author(s)
Makino, A. ; Inst. for Mater. Res., Tohoku Univ., Sendai, Japan

Melt-spun Fe85Si1-2B8-11P1-4Cu1 alloys have unusual hetro-amorphous structures which can transform to nanocrystalline structures composed of α-Fe grains with less than about 25 nm in size with crystallization. Especially, Fe85Si1-2B8-11P1-4Cu1 nanocrystalline soft magnetic alloys prepared by crystallizing an as-quenched nanohetero-amorphous phase including a large amount of extremely small α-Fe grains (less than 2-3 nm in size) exhibit high-B800 of 1.8-1.9 T (at 800 A/m) almost comparable to those of commercial oriented silicon steels and significantly higher than those of non-oriented silicon steels, along with extremely low core loss (W) which is 1/2-1/3 smaller than that of the highest-grade oriented silicon steel and about one-order smaller than those of non-oriented silicon steels at maximum flux density of 1.7 T. The nanocrystalline alloys with lower materials cost due to absence of rare-metals are expected to not only contribute to significant energy-saving and reduction of CO2 emission through reduction in W but also be useful to conserve the earth's resources and environment.

Published in:

Magnetics, IEEE Transactions on  (Volume:48 ,  Issue: 4 )