The Cation Distribution and Related Electrical Transport in ({\rm Fe}_{3-{x}}{\rm Mn}_{x}{\rm O}_{4}) Ferrite Films on MgO Substrate Grown by Molecular Beam Epitaxy

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

2 Author(s)
Lee, D.S. ; Electr. Eng. Dept., Da-Yeh Univ., Chunghua, Taiwan ; Chern, G.

We fabricated a series of Fe3-xMnxO4 (0 ≤ x ≤ 1.5) films by plasma-oxygen-assisted molecular beam epitaxy and did magnetic and electrical characterizations of these films. The magnetization measurement shows that the saturation magnetization (Ms) is consistent with the curve of minimum possible Ms. Accordingly, the present result suggests that Mn3+ replace Fe3+ mainly in the B-site, which is basically different from the bulk distribution mainly in the A-site. Resistance as a function of temperature in the range of 80-300 K is carried out for all films. The resistivity presents a typical Arrhenius temperature dependence with ρ = ρ0 exp(Ep/kBT) indicating that the transport is due to a hopping mechanism. The prefactor ρ0 increases with x in Fe3-xMnxO4 at smaller x but tends to level out at x >; 0.6, suggesting that the structure varies from a inverse spinel to a normal spinel in that the Fe2+/Fe3+ ratio remains constant at x >; 0.6. The activation energy Ep of electrical hopping remains a constant value ~50 meV at x <; 0.9 but abruptly rises up at x >; 0.9 and reaches 300 meV at x=1.5 , suggesting a semiconductor-insulator transformation. This increase in the activation energy may indicate a percolation limit which is different from the previous transformation observed in other ferrites such as Fe3-xMnxO4.