Wetting of bulk metallic glass forming liquids on metals and ceramics

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

3 Author(s)
Ding, Shiyan ; Department of Mechanical Engineering and Materials Science, Yale University, New Haven, Connecticut 06511, USA ; Kong, Jian ; Schroers, Jan

Your organization might have access to this article on the publisher's site. To check, click on this link:http://dx.doi.org/+10.1063/1.3615630 

Contact wetting angle of Pd43Ni10Cu27P20, Pt57.5Cu14.7Ni5.3P22.5, Au49Ag5.5Pd2.3Cu26.9Si16.3, and Zr57Nb5Cu15.4Ni12.6Al10 bulk metallic glass forming alloys have been determined on materials that are used in micro and nano fabrication. Employing the sessile drop technique at a temperature above the corresponding melting temperatures, three kinds of wetting behaviors are observed, spanning from θ ≈ 140°, over neutral wetting, θ ≈ 80°, to almost complete wetting, θ < 5°. The origin for complete wetting is the formation of an interface phase promoting wetting. Estimations of the contact wetting angles are presented for temperatures in the supercooled liquid region where micro and nano fabrication is typically carried out. Consequences of the observed wetting behaviors for nanoforming are discussed.