Surface Corrosion of Ti–16Si–4B Powder Alloy Implanted With Nitrogen by Plasma-Based Technique

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

5 Author(s)
Fernandes, B.B. ; Nat. Inst. for Space Res. (INPE), Sao Jose dos Campos, Brazil ; Ueda, M. ; da Silva Savonov, G. ; de Moura Neto, C.
more authors

Titanium materials with a new ternary phase, Ti6Si2 B, can be manufactured by high-energy ball milling and further sintering of titanium, silicon, and boron powders. In this paper, hot pressing was chosen to compact the granules and then prevent high porosity and grain coarsening during sintering. Subsequently, the surface of the Ti-16Si-4B (at.%) alloy was modified by nitrogen ion implantation using a plasma immersion technique. The marine corrosion behavior of this powder alloy was studied in this paper. Scanning electron microscopy and X-ray diffraction analyses were performed on the powders and alloys in order to observe phase compositions and morphologies. The morphology of sample surfaces was also observed by utilizing an atomic force microscope. The concentration profile of the detected elements has been investigated using Auger electron spectroscopy depth profiling. The results show that a shallow nitrogen-rich layer was obtained after implantation treatment. Potentiodynamic analyses showed that, with the nitrogen insertion, there is a significant reduction of the anodic current in almost the whole potential spam explored, meaning that the corrosion rate decreases when ion implantation is performed.