Energy release rate investigation for through silicon vias (TSVs) in 3D IC integration

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $13
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

6 Author(s)
Ming-Che Hsieh ; Ind. Technol. Res. Inst., Hsinchu, Taiwan ; Sheng-Tsai Wu ; Chung-Jung Wu ; Lau, J.H.
more authors

The technology of 3D IC integration is highly probable to achieve the demand for high performance, better reliability, miniaturization and lower-priced portable electronic products. Since the through silicon via (TSV) is the heart in 3D IC integration architectures, the reliability issues of TSV interconnects should be extremely concerned. Due to the large thermal expansion mismatch among the Cu, Si, and SiO2, the induced thermal stresses and strains can occur and become the driving forces for failures in TSV interconnects. Hence, the stress analyses and failure mode investigation for TSVs are in urgent need. Among the typical failures, the mostly common failure type is delamination, which will be caused when lower energy release rate (ERR) or higher critical stresses at interfaces are presented. In this study, the finite element modeling (FEM) for a symmetrical single in-line copper filled TSV with redistribution layer is illustrated. Two kinds of horizontal cracks that embedded in the interface of SiO2 passivation and Cu seed layer (Cu pad delamination cases) are introduced to realize the interfacial ERR, where is also the critical stress area that observed from finite element analysis. The significance of design parameters such as crack length, TSV diameter, TSV pitch, depth of TSV, SiO2 thickness and Cu seed layer thickness are also brought up. The methodology of design of experiments (DoE) has been adopted to capture the most important mechanical parameters of the TSV to comprehend the corresponding ERR. It is believed that these results would be helpful to avoid delamination of TSV interconnects in 3D IC integration.

Published in:

Thermal, Mechanical and Multi-Physics Simulation and Experiments in Microelectronics and Microsystems (EuroSimE), 2011 12th International Conference on

Date of Conference:

18-20 April 2011