[001]-oriented nonepitaxial growth in L10-ordered FePt thin film by SiO2 addition and rapid thermal annealing

Sign In

Cookies must be enabled to login.After enabling cookies , please use refresh or reload or ctrl+f5 on the browser for the login options.

Formats Non-Member Member
$31 $31
Learn how you can qualify for the best price for this item!
Become an IEEE Member or Subscribe to
IEEE Xplore for exclusive pricing!
close button

puzzle piece

IEEE membership options for an individual and IEEE Xplore subscriptions for an organization offer the most affordable access to essential journal articles, conference papers, standards, eBooks, and eLearning courses.

Learn more about:

IEEE membership

IEEE Xplore subscriptions

4 Author(s)
Narisawa, T. ; Department of Materials Science and Engineering, Akita University, 1-1 Gakuen-machi, Tegata, Akita 010-8502, Japan ; Hasegawa, T. ; Ishio, S. ; Yamane, H.

Your organization might have access to this article on the publisher's site. To check, click on this link: 

A highly L10-ordered FePt film with a crystalline [001] orientation was prepared by SiO2 addition and rapid thermal postannealing on an oxidized Si substrate. In order to clarify the mechanism of L10 ordering and the crystalline orientation of a nonepitaxial FePt film, we investigated the effect of the preparation conditions on the film structure. The crystalline quality was strongly dependent on the additive amount of SiO2; a high chemical order without the distribution of the chemical order and a nearly perfect [001] orientation were obtained at a SiO2 composition of 10 vol%. The nucleation of L10 grains with a high chemical order and a [001] orientation was observed from an initial phase transformation stage at a low annealing temperature. The as-deposited FePtSiO2 film consisted of a nanocrystalline structure in which SiO2 segregated at the grain boundaries; SiO2 diffused with the grain growth during thermal annealing. Because the in-plane tensile stress among the grains was a dominant origin for the [001] texture formation, two-dimensional grain growth with the annihilation of grain boundaries played a crucial role in the [001] ordering in nonepitaxial FePt films. It was also crucial to maintain a high stress during annealing, and the [001] ordering was enhanced by rapid heating.

Published in:

Journal of Applied Physics  (Volume:109 ,  Issue: 3 )